Asymmetry of domain nucleation and enhanced coercivity in exchange-biased epitaxial NiO/NiFe bilayers

Download: PDF (2,707 kB) Buy this article Export: BibTeX or EndNote (RIS)

V. I. Nikitenko, V. S. Gornakov, L. M. Dedukh, Yu. P. Kabanov, and A. F. Khapikov
Institute of Solid State Physics, Russian Academy of Sciences, 142432 Chernogolovka, Moscow District, Russia

A. J. Shapiro and R. D. Shull
Metallurgy Division, National Institute of Standards and Technology, Gaithersburg, Maryland 20899

A. Chaiken and R. P. Michel
Materials Science and Technology Division, Lawrence Livermore National Laboratory, Livermore, California 94551

Received 14 January 1998; published in the issue dated 1 April 1998

Magnetization reversal processes in epitaxial NiO/NiFe bilayers were studied using the magneto-optic indicator film technique. The influence of dislocations on these processes was determined. Remagnetization parallel to the unidirectional anisotropy axis proceeds by domain nucleation and growth, with nucleation center activity being asymmetric with respect to the applied field sign. Magnetization reversal in the hard axis direction occurs by incoherent rotation. The enhanced coercivity and asymmetric nucleation can be explained by taking into account domain wall behavior in the antiferromagnetic layer.

© 1998 The American Physical Society

URL:
http://link.aps.org/doi/10.1103/PhysRevB.57.R8111
DOI:
10.1103/PhysRevB.57.R8111
PACS:
75.70.Cn, 75.30.Et, 75.50.-y, 75.60.-d
 
< Previous Article | Next Article >